OLDER RATES

Material Date Sample ID Process parameters Measured with Result Rate
Al 20040513 Cristianne 6e-3mbar, 220mA RBS - 6.34A/nm
Al 20050324 Sample3 6e-3mbar, 200mA, 5mins X-ray 116nm 23.2nm/min
Al 20050628 Machiel 2.5e-3mbar, 200mA, 415V, 269deg, 6min X-ray 128nm (640A Xthal) 3.56 A/s (1.78 A/s)
Al 20060329 Chris 4e-3mbar, 200mA, 357V, 45deg AWAY from target, 15min X-ray 44.5nm (1180A Xthal) 2.97 nm/min (78.7 nm/min)
Al 20060913 13_9_6_5 4.0e-3 mbar, 200 mA, 5 min, tilted X-ray 110 nm 46.8 nm 22 nm/min
Al 20060918 18_9_6_1 4.0e-3 mbar, 200 mA, 5 min, tilted α-stepper 112-115 nm 45.9 nm 22.8 nm/min
Co 20111215 CoUHVcal 4.0e-3 mbar, 200 mA, 4 min X-ray 33.9 nm 8.48 nm/min
Co 20120208 CoUHV100mA 4.0e-3 mbar, 100 mA, 5 min X-ray 21.0 nm 4.20 nm/min
Co 20120209 CoUHV50mA 4.0e-3 mbar, 50 mA, 5 min X-ray 10.3 nm 2.06 nm/min
Co 20120716 UHV-Co-300s 4.0e-3 mbar, xxx mA, 300 s X-ray 44.1 nm 8.8 nm/min
Co 20120716 UHV-Co-300s 4.0e-3 mbar, xxx mA, 300 s X-ray 44.1 nm 8.8 nm/min
Co 20130301 Co-25mA 4.0e-3 mbar, 25 mA, 1800 s X-ray 23.5 nm 0.783 nm/min
Co 20130130 Co-100mA 4.0e-3 mbar, 100 mA, 485 s X-ray 29.2 nm 3.61 nm/min
Co 20130130 Co-200mA 4.0e-3 mbar, 200 mA, 300 s X-ray 41.5 nm 8.31 nm/min
Co 20130513 Co-100mA 4.0e-3 mbar, 100 mA, 600 s X-ray 34.79 nm 3.479 nm/min
Co 20130625 Co_10m 4.0e-3 mbar, 100 mA, 600 s X-ray 35.3 nm 3.53 nm/min
Co 20140321 Co_50nm 4.0e-3 mbar, 100 mA, 850 s, 45 deg X-ray 50.77 nm 3.58 nm/min
Cu 20120513 Cu 4.0e-3 mbar, 65 mA, 180 s X-ray 34.13 nm 11.37 nm/min
Cu 20111219 CuUHVcal 4.0e-3 mbar, 165 mA, 1.5 min X-ray 27.0 nm 18.0 nm/min
Cu 20120716 UHV-Cu-120s 4.0e-3 mbar, xxx mA, 120 s X-ray 70.1 nm 35.1 nm/min
Cu 20120716 UHV-Cu-120s 4.0e-3 mbar, xxx mA, 120 s X-ray 70.1 nm 35.1 nm/min
Cu 20130130 Cu 4.0e-3 mbar, 65 mA, 180 s X-ray 33.9 nm 11.30 nm/min
Cu 20120625 Cu_3m 4.0e-3 mbar, 65 mA, 180 s X-ray 32.2 nm 10.73 nm/min
CuNi 20070924 Cal_07_CuNi 4.0e-3 mbar, 70 mA, 20 min X-ray 47.7 nm 42.5 nm 2.4 nm/min
Cu_50Ni_50 20110712 CuNi_cal 4.0e-3 mbar, 70 mA, 20 min X-ray 40.2 nm - 2.0 nm/min
CuNi 20051130 CN1 4e-3mbar, 70mA, 760V, 270sec X-ray 10.9nm 0.40 A/s
CuNi (back of old one) 20061130 30_11_6_2 and 3 4e-3mbar, 70mA, 2 mins and 5mins Xray 5.2nm and 12.4nm (45 and 112A Xtal) Average 2.54 nm/min
FeMn 20060913 13_9_6_6 4.0e-3 mbar, 200 mA, 10 min X-ray 75 nm 49.3 nm 7.5 nm/min
FeMn 20060918 18_9_6_2 4.0e-3 mbar, 200 mA, 11 min α-stepper 75-80 nm 53.2 nm 7.1 nm/min
FeMn50/50 20080404 FeMn 4.0e-3 mbar, 200 mA, 3.5 min X-ray 75.6 nm 90.7 nm 21.6 nm/min
Fe_50Mn_50 20110712 FeMn_cal 4.0e-3 mbar, 200 mA, 5.0 min X-ray nm - nm/min
Ho 20130130 Ho 4.0e-3 mbar, 40 mA, 600 s X-ray 48.5 nm 4.85 nm/min
Nb 20130130 Nb 4.0e-3 mbar, 200 mA, 480 s X-ray 24.8 nm 3.1 nm/min
Nb 20030404 Sasha 6e-3mbar, 220mA X-ray - 6.19A/nm
Nb 20050125 Nb2 4e-3mbar, 220mA, 340V, 3min X-ray 22.5nm 1.1A/s
Nb 20050922 220905 4e-3mbar, 220mA, 360V, 10min X-ray 68nm 1.13A/s
Nb 20051507 Machiel 4.0e-3mbar, 220mA, 305V, 224deg, 15min X-ray 73nm (554A Xthal) 0.81 A/s (0.62 A/s)
Nb 20051111 Carla 4.0e-3mbar, 220mA, 224deg, 3min X-ray 21.26 1.18 A/s
Nb 20060913 13_9_6_3 4.0e-3 mbar, 220 mA, 10 min X-ray 71.8 nm 48.6 nm 7.2 nm/min
Nb 20060918 18_9_6_6 4.0e-3 mbar, 220 mA, 10 min α-stepper 74 nm 46.2 nm 7.4 nm/min
Nb 20070302 NbCal 4.0e-3 mbar, 220 mA, 4.2 min X-ray 26.0 nm 16.7 nm 6.2 nm/min
Nb 20070924 Cal_07_Nb 4.0e-3 mbar, 220 mA, 8 min X-ray 55.6 nm 33.8 nm 6.7 nm/min
Nb 20090709 Nb_Simon 4.0e-3 mbar, 220 mA, 4 min X-ray 27.8 nm 18.8 nm 6.7 nm/min
Nb 20121113 UHV-Nb-600s 4.0e-3 mbar, 200 mA, 600 s X-ray 31.8 nm 3.2 nm/min
Nb 20110713 NG 4.0e-3 mbar, 220 mA, 8 min X-ray 46.0 nm xx.x nm 5.75 nm/min
Nb 20120716 UHV-Nb-340s 4.0e-3 mbar, xxx mA, 340 s X-ray 23.6 nm 4.2 nm/min
Nb 20121113 UHV-Nb-600s 4.0e-3 mbar, 200 mA, 600 s X-ray 31.8 nm 3.2 nm/min
Nb 20120513 Nb 4.0e-3 mbar, 200 mA, 600 s X-ray 30.67 nm 3.067 nm/min
Nb 20120625 Nb_10m20s 4.0e-3 mbar, 200 mA, 620 s X-ray 28.1 nm 2.72 nm/min
Ni 20120625 Ni_5m 4.0e-3 mbar, 150 mA, 300 s X-ray 26.8 nm 5.36 nm/min
Ni 20140218 Ni 11min 4.0e-3 mbar, 100 mA, 11 min X-ray 37.6 nm 3.418 nm/min
PdNi 20040915 PN1 4e-3mbar, 200mA, 532V, 5min X-ray 69.4nm 13.88 nm/min
PdNi 20050125 P8 4e-3mbar, 200mA, 518V, 90sec X-ray 20.0nm 2.14 A/s
PdNi 20070302 PdNiCal 4.0e-3 mbar, 200 mA, 2.5 min X-ray 28.8 nm 35.2 nm 11.5 nm/min
PdNi 20100721 PdNionSi 4.0e-3 mbar, 100 mA, 10 min X-ray 50.8 nm 60.0 nm 5.1 nm/min
PdNi 20111215 PdNiUHVcal 4.0e-3 mbar, 160 mA, 4 min X-ray 63.9 nm 16.0 nm/min
PdNi 20120716 UHV-PdNi-150s 4.0e-3 mbar, xxx mA, 150 s X-ray 43.8 nm 17.5 nm/min
PdNi 20120716 UHV-PdNi-150s 4.0e-3 mbar, xxx mA, 150 s X-ray 43.8 nm 17.5 nm/min
Pt 20111215 PtUHVcal 4.0e-3 mbar, 120 mA, 4 min X-ray 27.3 nm 6.83 nm/min
Pt 20120513 Pt 4.0e-3 mbar, 120 mA, 300 s X-ray 46.22 nm 9.244 nm/min
Py 20040226 Christianne 4e-3mbar, 165mA X-ray - 1 nm/5.9sec
Py 20040809 Christianne 4e-3mbar, 165mA X-ray - 2.54A/nm
Py 20050317 Youri 6e-3mbar, 200mA, 4min48s X-ray 57.8nm 2.72A/nm
Py 20050628 Machiel 2.5e-3mbar, 165mA, 485V, 179deg, 10min X-ray 122nm (337A Xthal) 2.03 A/s (0.56 A/s)
Py 20060913 13_9_6_2 4.0e-3 mbar, 200 mA, 10 min, tilted X-ray 163 nm 42.2 nm 16.3 nm/min
Py 20060918 18_9_6_5 4.0e-3 mbar, 100 mA, 10 min, tilted α-stepper 80-84 nm 19.0 nm 8.2 nm/min
Py 20060918 18_9_6_3 2.5e-3 mbar, 165 mA, 10 min, tilted α-stepper 142-147 nm 36.6 nm 14.5 nm/min
Py 20070924 Cal_07_Py 2.5e-3 mbar, 165 mA, 3.3 min X-ray 45.5 nm 10.7 nm 13.7 nm/min
Py 20090401 Py2.5e-3mbar 2.5e-3 mbar, 165 mA, 3 min X-ray 30.9 nm - 10.3 nm/min
Py 20090401 Py4.0e-3mbar 4.0e-3 mbar, 165 mA, 3 min X-ray 27.9 nm - 9.3 nm/min